Characterisation of Calcium Phosphate Crystals on Calcified Human Aortic Vascular Smooth Muscle Cells and Potential Role of Magnesium

Loïc Louvet; Dominique Bazin; Janine Büchel; Sonja Steppan; Jutta Passlick-Deetjen; Ziad A. Massy

doi:10.1371/journal.pone.0115342

Abstract

Background

Cardiovascular disease including vascular calcification (VC) remains the leading cause of death in patients suffering from chronic kidney disease (CKD). The process of VC seems likely to be a tightly regulated process where vascular smooth muscle cells are playing a key role rather than just a mere passive precipitation of calcium phosphate. Characterisation of the chemical and crystalline structure of VC was mainly led in patients or animal models with CKD. Likewise, Mg²⁺ was found to be protective in living cells although a potential role for Mg²⁺ could not be excluded on crystal formation and precipitation. In this study, the crystal formation and the role of Mg²⁺ were investigated in an in vitro model of primary human aortic vascular smooth muscle cells (HAVSMC) with physical techniques.

Methodology/Principal Findings

In HAVSMC incubated with increased Ca x Pi medium, only calcium phosphate apatite crystals (CPA) were detected by Micro-Fourier Transform InfraRed spectroscopy (µFTIR) and Field Effect Scanning Electron Microscope (FE — SEM) and Energy Dispersive X-ray spectrometry (EDX) at the cell layer level. Supplementation with Mg²⁺ did not alter the crystal composition or structure. The crystal deposition was preferentially positioned near or directly on cells as pictured by FE — SEM observations and EDX measurements. Large µFTIR maps revealed spots of CPA crystals that were associated to the cellular layout. This qualitative analysis suggests a potential beneficial effect of Mg²⁺ at 5 mM in noticeably reducing the number and intensities of CPA µFTIR spots.

Conclusions/Significance

For the first time in a model of HAVSMC, induced calcification led to the formation of the sole CPA crystals. Our data seems to exclude a physicochemical role of Mg²⁺ in altering the CPA crystal growth, composition or structure. Furthermore, Mg²⁺ beneficial role in attenuating VC should be linked to an active cellular role.

Citation: Louvet L, Bazin D, Büchel J, Steppan S, Passlick-Deetjen J, Massy ZA (2015) Characterisation of Calcium Phosphate Crystals on Calcified Human Aortic Vascular Smooth Muscle Cells and Potential Role of Magnesium. PLoS ONE 10(1): e0115342. https://doi.org/10.1371/journal.pone.0115342

Academic Editor: Elena Aikawa, Brigham and Women’s Hospital, Harvard Medical School, UNITED STATES

Received: July 30, 2014; Accepted: November 22, 2014; Published: January 21, 2015

Copyright: © 2015 Louvet et al. This is an open access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited

Data Availability: All relevant data are within the paper and its Supporting Information files.

Funding: The funders (Fresenius Medical Care Deutschland GmbH) participated in part of the study design and revision of the final version of manuscript. They had no role in data collection, analysis, preparation of manuscript and decision to publish.

Competing interests: The external funders (Fresenius Medical Care Deutschland GmbH, a worldwide provider of dialysis products and therapies for patients with chronic kidney failure) participated in part of study design and revision of final version of manuscript. They had no role in data collection, analysis, preparation of manuscript and decision to publish. The authors declare J.P.-D. as a consultant to Fresenius Medical Care Deutschland GmbH. S.S. and J.B. are employees of Fresenius Medical Care Deutschland GmbH. Z.A.M. and D.B. have received research grants and honorarium from Fresenius Medical Care Deutschland GmbH. This statement does not alter the authors’ adherence to PLOS ONE policies on sharing data and materials.

Introduction

Patients suffering from atherosclerosis, diabetes and chronic kidney disease (CKD) often present with vascular calcification (VC) [1–3]. In adults with CKD including dialysis patients, cardiovascular disease including VC remains to be the leading cause of death. VC manifests itself as deposits of calcium phosphate complexes accompanied by phenotypical cell fate changes in both the intimal and medial layer of the large arteries including the aorta, the myocardium as well as cardiac valves. VC is clinically reflected by changes in parameters such as pulse pressure, coronary artery calcification, intima media thickness or pulse wave velocity [4, 5]. The process of VC is not fully understood, but likely to be multifactorial [6]. It appears to be a tightly regulated, active, cellular process rather than just a mere passive precipitation of calcium phosphate, that somewhat resembles normal bone formation. How the process of calcification is initiated has been the subject of several studies. Some results suggest that matrix calcification could be initiated through passive calcium phosphate deposition and that it could be the formation of calcium phosphate nanocrystals that triggers the osteogenic changes that are associated with the accumulation of extracellular, crystalline structures [7, 8], whereas other studies show that calcification could be initiated by the release of matrix vesicles and/or apoptotic bodies from (dying) VSMC that act as nucleation points for forming crystals [9].

Some studies focused on characterising the anatomical, chemical and crystalline structure of the calcium phosphate deposits in patients or animal models with CKD, but the results remain heterogeneous. A study in uraemic patients revealed hydroxyapatite in non-visceral and arterial calcification, whereas visceral calcification was identified as an amorphous or microcrystalline compound composed of calcium, magnesium and phosphorus [10]. Another study assessed mineral deposits in the aortic wall in calcitriol- and non-calcitriol-treated rodent models of uraemia-induced VC. Here, they were composed of amorphous calcium phosphate precipitate, apatite and also whitlockite in animals treated with calcitriol [11]. In contrast, an other investigation reported a colocalization of hydroxyapatite and whitlockite in three out of six tissue samples taken from iliac arteries of uraemic patients [12], whereas another recent study on tissue specimens from non–CKD and CKD stage 2–4 patients undergoing carotid endarterectomy for severe atherosclerosis showed that in microcalcifications most of the calcium phosphate was amorphous rather than mature apatite. Moreover, it revealed that the relative contributions of whitlockite and calcium phosphate to microcalcification differed between patients with normal and mildly impaired renal function: Whereas in the samples of patients with normal renal function, whitlockite and calcium phosphate contribute to the mineral phase to an almost identical extent, approximately two-thirds of the mineral consists of calcium phosphate in the patients with impaired renal function [13].

In the course of VC vascular smooth muscle cells (VSMC) that compose the medial layer of the vascular wall are playing a key role. Recently, the effect of magnesium on VSMC transformation and calcification was assessed in vitro as well in as in the aortas of rodents. Here, magnesium was able to inhibit the calcification process and attenuated osteogenic differentiation of cells as reflected through an increased expression of anti-calcification proteins such as matrix gla protein, osteopontin and bone morphogenetic protein 7 [14]. These findings were confirmed by Salem et al., who described correlations between magnesium, inhibition of VC in calcification-induced aortic rings of rats and clinical biomarkers [15]. To date, three studies directly addressed the effect of magnesium on VC of VSMC in vitro. Here, magnesium significantly reduced induced calcification both in bovine as well as human primary VSMC, downregulated known pro-calcification and upregulated anti-calcification markers towards restoring more physiological expression levels seen in uncalcified controls [16, 17, 18]. Moreover, an active, cellular, inhibitory role was attributed to magnesium as it was only able to exert its protective effect on living cells [17]. These findings do not exclude a potential passive role for Mg²⁺ ions in the onset of calcification, because in the presence of Mg²⁺ cumulating evidence shows that magnesium can have an inhibitory effect on hydroxyapatite formation and precipitation. Earlier in vitro work shows that magnesium is able to stabilize amorphous calcium phosphate and inhibits the formation of hydroxyapatite as well as calcium pyrophosphate dehydrate and calcium-acidic phospholipid-phosphate complexes [19–23]. In the literature, biological calcium phosphate crystals are often referred as hydroxyapatite leading this term to designate many complex compounds. Indeed, calcium phosphate hydroxyapatite is considered as a model compound for biological mineralization although its ideal formula has not actually been found in vivo. The composition of calcium phosphate apatite crystals has been shown to vary over a wide range due to the possibilities of anionic and cationic substitutions and the existence of different type of ion vacancies [24].

To our knowledge, for the first time, the crystal formation and the possible role of Mg²⁺ in VC through an in vitro model of primary human aortic vascular smooth muscle cells (HAVSMC) was investigated in this study. At this point, we have to underline that usual methods to gather information on the chemical nature of VC are based on staining procedures which display several limitations for identifying and quantifying apatite [25, 26]. All these limitations call for the need to combine usual techniques with physical techniques such as Scanning Electron Microscopy (SEM), Micro-Computerized Tomography, Micro-Fourier Transform InfraRed (µFTIR), RAMAN spectroscopies and X-ray fluorescence or X-ray scattering [27]. In this report, we developed an experimental procedure to culture cells on a support that was suitable to perform these techniques. The use of HAVSMC allows a direct assessment of the crystal formation process in a living system albeit under controlled conditions. In a novel way, the ultrastructure as well as the morphology of the calcium phosphate deposits directly on the culture cell layer were characterised with physical techniques such as Field Effect Scanning Electron Microscopy (FE—SEM), Energy Dispersive X-ray spectrometry (EDX) and µFTIR spectroscopy.

Material and Methods

All chemicals were purchased from Sigma unless otherwise stated.

Cell culture of HAVSMC

Primary human VASMC were isolated in our laboratory from explants of human aortic tissue obtained with appropriate ethical approval. The samples were obtained after aortic valve bypass surgery or other types of surgery on the aorta from patients with various cardiovascular diseases (Pr Caus, Pôle Coeur Thorax Vaisseaux, CHU Amiens, France). This protocol was approved by the Ethics Committee that is “Comité de Protection des Personnes (CPP) Nord-Ouest II” under ID #2009/19 to collect aortas and is valid for any experimental procedure. Briefly, as approved by the CPP (i.e. French Ethical Committee), the donors receive before surgery an oral and a written information explaining that if they don’t give their refusal, their aorta will be used for experimental purposes. Indeed, in regard to French law, the aorta is once removed considered as biological waste. Consequently, a written consent from the donor is not required. The investigations were performed according to the principles outlined in the Declaration of Helsinki for use of human tissue or subjects. The aortas were anonymized once removed from the donors in the surgical block and the samples were labelled with a number later in the laboratory for experimental convenience. The donors could not then be identified. As previously described [17], medial tissue was separated from segment of human aorta after removal of endothelium. Small pieces of tissue (1–2 mm²) were placed in culture dish in Dulbecco’s Modified Eagle’s Medium (DMEM) supplemented with 15% of fetal bovine serum (FBS, Dominique Dutscher), 4.5 g of glucose, 1 mmol/L of pyruvate, 100 U/mL of penicillin, and 100 µg /mL of streptomycin in a 5% CO2 incubator at 37°C. Cells that migrated from explants were collected when confluent. The cells were maintained in DMEM supplemented with 15% FBS, the medium was replaced twice a week. HAVSMC were identified by their typical hill and valley morphology, and purity of the primary cell culture was further checked by immunocytochemistry using a monoclonal antibody against the α-smooth muscle actin protein 1A4 (Acta 2) (Santa Cruz Biotechnology). α-smooth muscle actin 1A4 is an isoform typical of smooth muscle cells (SMC) and is present in high amounts in vascular SMC [28]. The cells were used between passages 6 and 10, during which time they were able to calcify. HAVSMC were pre-tested for calcification on classical cell culture plates prior use in any experimental set. Cells isolated from 4 independent donors were tested alternatively depending on the availability of cells requested for the various experiments. For calcification assays, cells were seeded at 150 000 cells / well on precut MirrIR slides (Kevley Technologies) placed in 6-well plates. Cells were treated for the indicated times (i.e. 14 and 18 days) with various media conditions from 2–3 days after plating.

Calcification assays and sample preparation on MirrIR slides

MirrIR slides were cut into 20×25-mm pieces, sterilised in ethanol and dried in a laminar flow hood before use with cellular culture. To improve cell attachment and survival of HAVSMC on MirrIR slides, the slides were coated with gelatine 0.2% overnight in the incubator. The slides were then placed in 6-well plates while removing excess of gelatin solution, before seeding the slides with the cell suspension. The cell viability and attachment were greatly improved without affecting spectroscopic assays [29] comparing to cell growth on uncoated slides.

Calcification assays were conducted in 1% FBS DMEM. The control condition was incubated with 1% FBS DMEM only. DMEM medium is initially containing 0.9 mM of Pi, 1.8 mM of Ca²⁺ and 0.8 mM of Mg²⁺. When indicated, the media Pi and Mg²⁺ concentrations were increased using NaH₂PO₄ and MgCl₂ supplementation, respectively. To induce calcification, Pi concentration was initially increased to reach 3mM during 10 and 14 days as performed in a previous study [17]. The weakness of the signal to detect Ca / Pi deposits in this experimental set (data not shown) led us to increase the Ca x Pi product for further experiments and to extend the incubation time in calcifying conditions to 14, 18 and 21 days. The Ca x Pi product in calcifying conditions was enhanced from 5.4 (initially with 3 mM Pi) to reach 7.2, using two different approaches: the samples were treated with 4 mM Pi (labelled Pi4), or they were incubated with a mix of 3 mM Pi and 2.4 mM Ca²⁺ (labelled PiCa). All experiments are summarized in table 1. For both types of calcification induction, Mg²⁺ was assessed at various concentrations including 1.5, 2 and 5 mM of total Mg²⁺ (labelled Mg 1.5, 2 and 5 respectively). At the end of the experiment, media were removed and cells were fixed using a 3.7% formaldehyde solution at room temperature for 15 minutes. As detailed in [30], the use of formaldehyde does not interfere with µFTIR. After removal of formaldehyde, the samples were dried and suitable for the µFTIR analysis. For some samples, a Von Kossa was performed before the analysis to allow a better visualization of the calcified areas.

Download:

Table 1. Identification of the samples studied through µFTIR experiments.

https://doi.org/10.1371/journal.pone.0115342.t001

For the Von Kossa staining, the cells were rinsed and incubated with a 5% AgNO₃ solution for 30 min. Cells were further rinsed with water, incubated for 5 min in a photographic revelation solution, washed with water, then incubated 5 min with a 5% sodium thiosulfate solution to remove unreacted silver, washed again in water and finally dried. To evaluate passive Ca / Pi deposition, precut MirrIR slides were incubated as it was for samples with cells, slides were finally dried without further fixation.

Specific controls

Media from the various experimental conditions were assessed for correct calcium, phosphorus and magnesium levels using an ADVIA 1800 Siemens autoanalyzer (Siemens Healthcare Diagnostics). No significant change in pH was observed at the various Pi and Mg²⁺ concentrations. This excludes a potential role of medium acidification in the observed decrease of mineralization. We excluded the potential action of the chloride ions in the MgCl₂ salt used for these experiments on calcification reduction in a previous study [17].

Field Effect Scanning Electron Microscope (FE—SEM)

A Zeiss SUPRA55-VP SEM was used for observation of microstructure. This field-effect “gun” microscope (FE-SEM) operates at 0.5–30 kV. High-resolution observations were obtained by 2 secondary electron detectors: an in-lens SE detector and an Everhart-Thornley SE detector. To maintain the integrity of the samples, measurements were taken at low voltage (between 0.5 and 2 kV) without the usual deposits of carbon at the surface of the sample. Energy Dispersive X-ray (EDX) experiments was also performed. In order to perform Ca²⁺ cartography, the FE-SEM operates at 12. kV.

Energy Dispersive X-ray spectrometry (EDX)

The EDX detector is equipped with an ultra-thin window allowing detection of light elements. EDX provided the elemental composition of the solid phases and helped to identify them (point analyses and elemental maps).

FTIR spectroscopy

µFTIR measurements were carried out on IN10 experimental device and also performed on an IN10MX microscope (Thermo Scientific) to allow recording of large maps. All spectra were collected in ultrafast mode using a 50 μm × 50 μm aperture. The spectra were collected in the 4000–800 cm^-1 mid-IR range at a resolution of 16 cm^-1 with one spectrum per pixel. Data analysis of IR spectra and chemical images was performed using OMNIC software (Thermo Scientific). In order to estimate the overall extent of mineralized matrix over the samples as well as its chemical nature, a first set of maps was performed (2000 µm x 4500 µm), then large maps were collected to allow an extended overview of the different conditions (3700 μm x 7700 μm). Due to the extended acquisition times to picture the maps, several maps were divided for convenience in 2 or 4 areas depending on the initial map size. Different options were applied to build the map: maximum of the peak without background estimated with different limits, evaluation of the area between different limits without background estimated with different limits. The maps which are presented correspond to the area calculated between 1000 and 1100 cm^-1 without backgrounds. Data analysis of IR spectra and chemical images was performed using OMNIC software (Thermo Scientific).

Results

Preliminary results

Control conditions, i.e. samples with DMEM 1% FBS only, were assessed and showed a lack of characteristic FTIR signals corresponding to any of the Ca / Pi precipitates (amorphous carbonated calcium phosphate, whitlockite, hydroxyapatite…). Concerning the samples stained with Von Kossa, it appeared that this staining was not suitable for FTIR microspectroscopy on cell layer calcifications of our HAVSMC. While Von Kossa staining indicates the possible presence of calcium phosphate precipitates, µFTIR spectra clearly demonstrated that such dark deposits are not correlated to the presence of mineralized matrix. Indeed, no specific signal of Ca / Pi precipitates were detected following the staining regardless of the condition or incubation time observed (data not shown). Such observation is in line with previously published results [25]. In another experimental set, incubation time under calcifying conditions was extended to 21 days. However, results are presented in the S1 Fig. (IIA and IIB) but the long incubation time adversely affected the cell viability just as the massive mineral deposits observed prevented a discrimination between the different conditions. In this case, the thickness and the extent of the calcifications were too high to perform a reliable analysis or mapping of the FTIR measurement.

Ca²⁺ and Pi induce the formation of hydroxyapatite crystals on HAVSMC cell layer

Regarding the nature of the mineral deposition, the characteristic absorption bands of the different calcium phosphate compounds are well assigned [31, 32]. A shoulder in the ν3 (P-O stretching vibration mode) absorption band explicitly indicates the presence of a carbonate calcium phosphate compound. Thus, major absorption bands are observed at 1037 cm^-1 for apatite and 1068 cm^-1 for amorphous carbonate calcium phosphate. In the case of whitlockite, two major absorption bands exist (1080 cm^-1 and 1025 cm^-1). As shown in Fig. 1, a single band corresponding to calcium phosphate apatite (CPA) (Ca_{10−x+u□x−u}(PO4)_6−x(CO3)_x(OH)_2−x+2u with □ corresponding to vacancy, x≤2 and u≤x/2) crystals was detected in samples containing 3 mM Pi and 2.4 mM Ca²⁺ (sample PiCa) after 14 (data not shown) and 18 days (Fig. 1: Ib, Id) in calcifying condition. The same characteristic band was observed in samples containing 4 mM of Pi (S1 Fig.: Ia and Ic, respectively for 14 and 18 days in calcifying conditions). This means that the nature of the crystal was not influenced by the way we increased the Ca x Pi product to reach 7.2. By looking closely at the µFTIR profiles, a keen observer could notice that the peaks corresponding to CPA could not be perfectly superimposed. This fact is mainly due to the nature of the sample. More precisely, biological objects like mammalian cells could cause slight peak shifts or deviations compared to what is theoretically expected [33, 34, 35].

Download:

Figure 1. Typical optical image and mapping (scale from blue to red with increasing concentration), and FTIR spectra of crystals generated in Pi 4 or PiCa samples without or in presence of a total concentration of 2 mM of Mg²⁺.

Ia) Optical image, and corresponding Ib) typical FTIR spectra, Ic) Optical image and corresponding Id) typical FTIR spectra of sample PiCa. IIa) Optical image and corresponding IIb) typical FTIR spectra, IIc) Optical image and corresponding IId) typical FTIR spectra of sample PiCa Mg2.

https://doi.org/10.1371/journal.pone.0115342.g001

Mg²⁺ does not modify Ca / Pi crystal structure and composition

Several publications show that the incorporation of foreign ions into hydroxyapatite structure can affect its crystallinity, morphology, lattice parameters, and stability [36, 37, 38]. Among them Mg²⁺ is known to inhibit the synthesis of hydroxyapatite and promote the formation of whitlockite in acellular systems [39, 40]. Therefore, HAVSMC were incubated under both calcifying conditions (Pi4 and PiCa) whilst Mg²⁺ was added to reach various final concentrations (1.5, 2 and 5 mM) during 14 (S1 Fig.: Ib) and 18 days. As shown in Fig. 1 (IIb, IId), the collected µFTIR spectra are pointing towards the presence of a single apatite-typical band regardless of the assessed Mg²⁺ concentration or calcifying condition (for Pi4 samples containing Mg²⁺; please see the S1 Fig.: Id). Absorption bands corresponding to whitlockite (Ca₉Mg(HPO₄)(PO4)₆) were not detected in our samples meaning that the nature of the crystal was not affected by the presence of Mg²⁺. The µFTIR spectrum IIb in Fig. 1 tends towards the wavelength values of amorphous carbonate calcium phosphate. In addition to a slight peak shift that could be caused by the nature of the sample, this deviation could also reflect the presence of amorphous carbonate calcium phosphate mixed with CPA. Nevertheless, it would be an overstatement to impute the detection of amorphous carbonate calcium phosphate to the presence of magnesium because amorphous carbonate calcium phosphate is sporadically detected regardless of the presence of magnesium and does not represent the main crystal of interest here. Yet, a prior deposition of amorphous carbonate calcium phosphate is occurring during the CPA crystal formation process and throughout the crystal growth. As shown in the S1 Fig. (Ia, Ib, Ic, Id, IIAc, IIBc), the incubation time had no influence on the final crystal nature regardless of the condition. At 14, 18 or 21 days, the spectra are corresponding to CPA in Pi4 samples both in presence and absence of magnesium. It is of note that for 21 days samples (S1 Fig.: IIA and IIB) we restricted the map (S1 Fig.: IIAa, IIBa) to detect reliable µFTIR spectra. As mentioned in the preliminary results section, the calcifications were massive. These experimental conditions made it difficult to detect a reliable µFTIR peak and prevented a reliable µFTIR mapping. These results led us to consider the samples at earlier times of incubation in calcifying conditions to realise the µFTIR mapping.

Location of calcium phosphate apatite on HAVSMC cell layer

To reveal the CPA distribution on the MirrIR slide surface, µFTIR maps were performed on samples incubated for 14 (data not shown) and 18 days under both calcifying conditions and Mg²⁺ supplementation as shown in Fig. 2. These maps are showing that the calcium phosphate deposits were not diffusely distributed but clearly appeared as spots located directly on the cells or in close vicinity thereof. No deposits were found in great spatial distance from any cellular feature. Similar spots were found regardless of the assessed calcifying condition and the supplemented Mg²⁺ concentrations (to reach 2 and 5 mM). This finding was further confirmed using Field Effect Scanning Electron Microscope (Fig. 3A) combined with Energy Dispersive X-ray spectrometry observations. In order to gather information regarding the spatial repartition of Ca²⁺ and Mg²⁺ cations as well as Pi anions, EDX experiments were performed. In Fig. 3B, purple (for Pi) and red (for Ca²⁺) maps perfectly matched, revealing a co-localization of Pi and Ca²⁺ in the same structure. Observations were similar regardless of the assessed Mg²⁺ concentration or the calcifying condition (data not shown for PiCa with or without supplemental Mg²⁺). Moreover, a supplemental deposit of Mg²⁺ apart from the one incorporated in the support was not detected by EDX avouching its absence from calcium phosphate deposits (data not shown). FE-SEM pictured clearly the presence of calcification preferentially positioned on cells (Fig. 3A and 3B) regardless of the assessed Mg²⁺ concentration or the calcifying condition (data not shown for PiCa with or without supplemental Mg²⁺). Characterizing the size and the shape of the CPA particles remained laborious because of their diversity. As shown in Fig. 3A, small round deposits were observed with sizes starting from approximately hundreds of nm to dozens of µm. Some of the more prominent deposits are pictured in Fig. 3B. They sized around hundreds of µm, their shapes were heterogenous and associated to the cellular layout.

Download:

Figure 2. µFTIR maps obtained with calcium phosphate apatite features were collected for samples: PiCa, PiCa Mg2, PiCa Mg5, Pi4, Pi4 Mg2, Pi4 Mg5.

The scale bar corresponds to 500 µm while the amplitude is between 0 and 10. Due to extended acquisition times, some maps were divided in 2 areas. The map size is 2000 µm x 4500 µm.

https://doi.org/10.1371/journal.pone.0115342.g002

Download:

Figure 3. (A) SEM cartography of sample Pi4 Mg2 obtained with a magnification of 400 at 1 KeV (B) spatial distribution of Pi (purple maps), spatial distribution of Ca2+ (red maps) as obtained by EDX and SEM cartography (right pictures) obtained at 12 KeV for samples Pi4, Pi4 Mg2 and Pi4 Mg5.

https://doi.org/10.1371/journal.pone.0115342.g003

Passive Ca / Pi deposition on MirrIR slides

The passive Ca / Pi deposition was evaluated on MirrIR slides without cells. The slides were incubated as it was for samples with cells. Unlike to what was observed with living cells, the deposits were uniformly in nature and appeared far more prominently in conditions with increasing concentrations of Mg²⁺ (S2 Fig.).

Effect of Mg²⁺ on crystal formation

As detailed above, µFTIR maps were performed to reveal where CPA deposition was preferentially occurring (Fig. 2). Looking closely at these maps, it appeared that raising Mg²⁺ up to 5 mM during 18 days seemed to reduce the number and intensity of CPA peaks compared to the calcifying conditions alone (Pi4 or PiCa). At day 14, such influence of Mg²⁺ was not noticeable (data not shown). Larger maps were then performed for the Pi4, Pi4 Mg2 and Pi4 Mg5 samples at day 18 to confirm this finding. In Fig. 4, the expanded µFTIR maps show a heterogeneous spatial repartition of CPA. Calcifications are present on all samples although the map corresponding to the condition containing 5 mM of Mg²⁺ is showing less numerous spots and is exhibiting CPA peaks of weaker intensities. It is of note that the µFTIR maps corresponding to the CPA signal represent a qualitative analysis of the calcium phosphate deposit and should not be interpreted as a quantitative analysis.

Download:

Figure 4. Large µFTIR maps obtained with Ca apatite features (between 1000cm-1 and 1100 cm-1) were collected for samples Pi4, Pi4 Mg2, Pi4 Mg5.

The scale bar corresponds to 1000 µm while the amplitude is between 0 and 10. Due to extended acquisition times, some maps were divided in 4 areas. The map size is 3700 µm x 7700 µm.

https://doi.org/10.1371/journal.pone.0115342.g004

Discussion

For the first time, the nature of the Ca / Pi deposits was described using physical techniques such as SEM, µFTIR, and EDX in in vitro induced mineralization by assessing directly the cell layer of primary HAVSMC. Previously, cell directed Ca / Pi deposition was inadequately studied and indirectly analysed in vascular cell culture models. For instance, Villa-Bellosta et al. recently performed X-ray diffraction, scanning electron microscopy, energy dispersive spectroscopy and transmission electron microscopy on ground powders from rat aorta smooth muscle cells [7], which only partly allow to draw conclusions about the cellular involvement in the initiation and development of the calcifications. Identically, Sage et al. assessed high Pi medium Ca / Pi nanocrocrystal pellets, but not crystals taken directly from the cell culture supernatant or the cell layer, with scanning electron microscopy, energy-dispersive spectroscopy and atomic force microscopy [8]. Nevertheless, Ca / Pi deposition was never studied directly within a cultured cell layer context. Moreover, the potential role of magnesium on the nature, formation, structure of nanocrystals has never been investigated with physical techniques at the cellular level.

The first major result was on the nature of the mineral deposition that was found in our HAVSMC incubated with increased Ca x Pi medium. Raising Pi alone or altogether with Ca²⁺ led to the same final calcium phosphate crystal structure: calcium phosphate apatite (CPA). CPA, which is the mostly found biological apatite is a non-stoichiometric apatite (Ca_{10−x+u□x−u}(PO4)_6−x(CO3)_x(OH)_2−x+2u with □ corresponding to vacancy, x≤2 and u≤x/2): the presence of anionic (OH⁻) and cationic (Ca²⁺) vacancies has been evidenced compared to stoichiometric hydroxyapatite (Ca₅(PO4)₃(OH)) [27]. In biological systems, the term hydroxyapatite is given extensively to these kinds of apatites. CPA is the bone-like mineral that is commonly found in cultured osteoblastic models and is a marker of bone formation in vitro [25]. In the literature, VC was generally assumed to be composed mainly of hydroxyapatite [41]. More than a decade ago, several investigations demonstrated that coronary calcifications were already present in young dialysis patients, were progressing rapidly and were associated to a decreased survival [42, 43, 44]. Recently, the nature of arterial wall calcification from atherosclerotic and uremic patients was investigated more accurately with state-of-the-art physicochemical methods [12, 13, 45]. The results from these studies are showing that, apart from CPA, whitlockite (Ca₉Mg(HPO₄)(PO4)₆) can also be found together with CPA in microcalcifications of arteries, but CPA is most prevalent in CKD patients. Likewise, similar results were found in arteries of CKD animal models [11]. In cell culture models, hyperphosphatemia or increased Ca x Pi lead to a transformation of vascular smooth muscle cells that allows mineral deposition. The studies from Sage et al. and Villa-Bellosta et al. are in line with our results as they reported the presence of CPA in respectively ground powders of mineral matrix and in high medium Pi centrifuged Ca / Pi nanocrystal pellets from rodent VSMC [7, 8]. In summary, our results are strengthening the hypothesis that a bone-like mineralized matrix is formed during the course of VC in the arterial wall.

In a previous study [17], we found that Mg²⁺ was able to partially prevent Pi-induced calcification in HAVSMC. This protective role was mediated by live cells through a modulation of various calcification markers. These findings did not exclude a potential passive role for Mg²⁺ in the onset of calcification, by either inhibiting nucleation, growth of calcium phosphates or altering crystal composition and structure. Several in vitro works studied the influence of Mg²⁺ on calcium phosphate crystal initiation and growth in acellular systems. As underlined by Salimi et al. [39], Mg²⁺ cations have a marked inhibitory effect on hydroxyapatite growth. As discussed by Hamad and Heughebaert [46], traces of Mg²⁺ have a significant effect on nucleation and growth of calcium phosphates. These ions delay the conversion of amorphous calcium phosphates to more stable apatite-like phases [47]. These results could not be validated in our cellular system, albeit passive deposition was evaluated on MirrIR slides without cells. With respect to the tested conditions, the deposits were more pronounced than their respective cellular counterpart and were far more prominent in conditions with increasing concentrations of Mg²⁺ (data not shown). This observation rules out the possibility of a direct physicochemical inhibition of Mg²⁺ on nucleation or growth of CPA in our model. Concerning the Mg²⁺ influence on the crystal structure and composition, several publications show that the incorporation of foreign ions into hydroxyapatite structure can affect its crystallinity, morphology, lattice parameters, and stability [36, 37, 38]. Among them, Mg²⁺ is known to inhibit the synthesis of hydroxyapatite and promote the formation of whitlockite in acellular systems [39, 40]. In the presence of calcifying HAVSMC, regardless of the tested conditions, only CPA was detected using µFTIR in our samples even when 5 mM of Mg²⁺ was added. The passive deposition on MirrIR slides without cells did not yield the formation of withlockite even in presence of Mg²⁺ (data not shown). Succinctly, Mg²⁺ was not able to modify the crystal structure in our experimental setup. Our data are strongly reinforcing recent findings from De Schutter et al. that assessed a rat model of uremia treated with a magnesium-based phosphate binder [48]. VC was analysed in aortas as well as in femoral and carotid arteries using synchrotron X-ray µ-fluorescence and X-ray µ-diffraction. Uremic animals developed severe VC that was reduced in the aortas of animals of the Mg²⁺-containing phosphate binder group. Yet, the synchrotron analysis of VC indicated that mineral precipitates exclusively consisted of calcium hydroxyapatite. None of the samples contained whitlockite or any other type of calcium phosphate deposits in uremic rats regardless of the treatment. These findings strongly support a previous report by Massy et al. that analyzed VC in atheromatous lesions of ApoE^-/- uremic mice with FTIR. In their animal model, VC was composed of calcite and hydroxyapatite [49]. Shortly, supplemental Mg²⁺ was not able to alter the crystal structure neither in cellular nor in animal models. Taken together, our results suggest that the Mg²⁺ beneficial effects on VC are bound to cellular activities rather than physicochemical modifications of the calcium phosphate crystal.

The spatial distribution of the CPA crystals was investigated using µFTIR maps as well as FE-SEM combined with EDX spectrometry observations. The complete set of data led us to conclude that calcification occurs mainly as CPA spots located close to or directly on the HAVSMC bodies. In our experimental setup, CPA deposition was massive and the various crystal sizes start at the nm scale to largely exceed the µm scale. In this report, we are dealing with microcrystals rather than nanocrystals. For the small deposits, the crystals looked round while they took the shape of the cells in the larger ones, suggesting that respectively matrix vesicles or apoptotic bodies may serve as calcification nidus [50]. The calcification process seems more advanced in our work than in the studies that characterized nanocrystals in rodent VSMC cultures [7, 8]. Moreover, our experiments are highlighting a potential beneficial effect of Mg²⁺. At 5 mM, Mg²⁺ was noticeably able to reduce the number and intensities of CPA µFTIR spots. However, this observation must be taken with caution since only a qualitative analysis was performed. Combined with the results from our previous study [17], it is reasonable to think that this decrease of CPA spots might be linked to the improvement of HAVSMC viability, the modulation of calcification markers or is likely to be bound to cellular activities attributable to Mg²⁺.

As noted above, we conducted preliminary experiments to optimize the detection of mineralized matrix by µFTIR. Indeed, Ca / Pi concentrations were raised and incubation time was extended compared to the initial experimental setup published in [17]. We hypothesize that these modifications were imposed by the nature of the MirrIR slide support which is physically different compared to the standard cell culture plastic used in the previous study. During these tests, Von Kossa staining was assessed to allow a better visualization of mineralized deposits to easily target them for µFTIR analysis. Nevertheless, analysis of the dark deposits failed to detect any of Ca / Pi precipitates of interest. As the principle of Von Kossa staining is a chemical reaction in which silver ions react with phosphate, the resulting product is altered in its chemical nature which could adversely prevent from its detection by µFTIR. Anyway, none of the Von Kossa processed samples displayed Ca / Pi deposits detectable by µFTIR. Our results are confirming Bonewald et al. observations that reported a discrepancy between Von Kossa stained darkened nodules and the detection of hydroxyapatite. Among various calcifying models, the darkened nodules produced in MC3T3-E1 cells were tested as bulk samples using a FTIR spectrometer and failed to display features of Ca / Pi minerals. Transmission electron microscopy confirmed this finding. Consequently, the Von Kossa staining was withdrawn from our study as it appeared not suitable to perform the various physical analyses carried out in the present work.

The main limitation of this study lies in the rather limited number of samples that were assessed. This limitation is mainly due to: firstly, the requested/allowed time for the various physical techniques that were performed; and secondly, to the restricted number of cells that were available for the various experimental conditions because the primary cell cultures could not be expanded sufficiently to repeat each experiments several times. This clearly forbade us to realize a quantitative and statistical analysis of CPA spots that were detected between the various conditions. Furthermore, an accurate biochemical assessment of Ca²⁺ could not be performed from our samples because of the nature of the MirrIR slides that already include Ca²⁺. For these reasons, only a qualitative analysis of the composition, structure and distribution of the Ca / Pi crystals is presented here. Nevertheless, we succeeded in developing an experimental procedure to perform µFTIR / EDX / FE—SEM directly at the cell layer level in cultured HAVSMC. Consequently, this report might contribute largely to develop direct assessment of cellular models with physical techniques which is actually not common when browsing the bibliography.

In summary, our data are excluding a physicochemical role of Mg²⁺ in inhibiting the crystal growth or in altering the calcium phosphate crystal composition or structure in an in vitro model of HAVSMC culture. Furthermore, the observed qualitative reduction of CPA spots should be linked to an active cellular role of Mg²⁺ in attenuating VC. Whether the in vitro data collected in the present study also have relevance in clinical setting is matter of additional works. The use of magnesium as a drug to lower serum calcium and phosphorus and its effect on outcomes in CKD patients was detailed in [51]. To our knowledge, magnesium-containing phosphate binders have not yet been investigated for quantitative VC reduction in a controlled, prospective clinical setting. Likewise, supplemental in vitro investigations are currently ongoing and will further elucidate the cellular mechanisms by which Mg²⁺ is able to prevent VC.

Supporting Information

S1 Fig. I. Typical mapping (scale from blue to red with increasing concentration), optical image and FTIR spectra (from left to right, respectively) of crystals generated in Pi4 calcifying condition with or without magnesium (Mg2) at day 14 and day 18 of incubation representing: Ia, sample Pi4 at day 14; Ib, sample Pi4 Mg2 at day 14; Ic, sample Pi4 at day 18; Id, sample Pi4 Mg2 at day 18.

The scale bar corresponds to 500 µm. II. Typical mapping (scale from blue to red with increasing concentration), optical image and FTIR spectra of crystals generated in Pi 4 calcifying condition with or without magnesium (Mg2) at day 21 of incubation representing: IIA, a) Typical mapping (scale from blue to red with increasing concentration), b) Optical image, and c) typical FTIR spectra of sample Pi4; IIB, a) Typical mapping (scale from blue to red with increasing concentration), b) Optical image, and c) typical FTIR spectra of sample Pi4 Mg2.

https://doi.org/10.1371/journal.pone.0115342.s001

(PDF)

S2 Fig. µFTIR maps (scale from blue to red with increasing concentration) of crystals generated in Pi4 or PiCa calcifying condition with or without magnesium (Mg2 and Mg5) at day 18 of incubation.

The map size is of 3000 µm x 4000 µm.

https://doi.org/10.1371/journal.pone.0115342.s002

(PDF)

Acknowledgments

The authors thank Pr Caus and the ‘Service de Chirurgie Cardiaque, Pôle Coeur Thorax Vaisseaux, CHU Amiens, France’ for their contribution in this work. This study was supported by Fresenius Medical Care Deutschland GmbH, Germany.

Author Contributions

Conceived and designed the experiments: LL DB ZAM. Performed the experiments: LL DB. Analyzed the data: LL DB ZAM. Contributed reagents/materials/analysis tools: LL DB. Wrote the paper: LL DB JB SS JPD ZAM.

References

1. Takasu J, Budoff MJ, Katz R, Rivera JJ, O’Brien KD, et al. (2010) Relationship between common carotid intima-media thickness and thoracic aortic calcification: the Multi-Ethnic Study of Atherosclerosis. Atherosclerosis 209: 142–6. pmid:19782983
- View Article
- PubMed/NCBI
- Google Scholar
2. Ishiyama M, Suzuki E, Katsuda J, Murase H, Tajima Y, et al. (2009) Associations of coronary artery calcification and carotid intima-media thickness with plasma concentrations of vascular calcification inhibitors in type 2 diabetic patients. Diabetes Res Clin Pract 85: 189–96. pmid:19497632
- View Article
- PubMed/NCBI
- Google Scholar
3. Braun J, Oldendorf M, Moshage W, Heidler R, Zeitler E, et al. (1996) Electron beam computed tomography in the evaluation of cardiac calcification in chronic dialysis patients. Am J Kidney Dis Mar;27(3):394–401.
- View Article
- Google Scholar
4. London GM, Guerin AP, Marchais SJ, Metivier F, Pannier B, et al. (2003) Arterial media calcification in end-stage renal disease: impact on all-cause and cardiovascular mortality. Nephrol Dial Transplant 18: 1731–40. pmid:12937218
- View Article
- PubMed/NCBI
- Google Scholar
5. Noordzij M, Cranenburg EM, Engelsman LF, Hermans MM, Boeschoten EW, et al. (2011) Progression of aortic calcification is associated with disorders of mineral metabolism and mortality in chronic dialysis patients. Nephrol Dial Transplant 26: 1662–9. pmid:20880929
- View Article
- PubMed/NCBI
- Google Scholar
6. Moe SM, Chen NX (2004) Pathophysiology of vascular calcification in chronic kidney disease. Circ Res 95: 560–7. pmid:15375022
- View Article
- PubMed/NCBI
- Google Scholar
7. Villa-Bellosta R, Millan A, Sorribas V (2011) Role of calcium-phosphate deposition in vascular smooth muscle cell calcification. Am J Physiol Cell Physiol 300: C210 C220. pmid:20881235
- View Article
- PubMed/NCBI
- Google Scholar
8. Sage AP, Lu J, Tintut Y, Demer LL (2011) Hyperphosphatemia-induced nanocrystals upregulate the expression of bone morphogenetic protein-2 and osteopontin genes in mouse smooth muscle cells in vitro. Kidney Int 79: 414–22. pmid:20944546
- View Article
- PubMed/NCBI
- Google Scholar
9. Reynolds JL, Joannides AJ, Skepper JN, McNair R, Schurgers LJ, et al. (2004) Human vascular smooth muscle cells undergo vesicle-mediated calcification in response to changes in extracellular calcium and phosphate concentrations: a potential mechanism for accelerated vascular calcification in ESRD. J Am Soc Nephrol 15:2857–67. pmid:15504939
- View Article
- PubMed/NCBI
- Google Scholar
10. Contiguglia SR, Alfrey AC, Miller NL, Runnells DE, Le Geros RZ (1973) Nature of soft tissue calcification in uremia. Kidney Int 4: 229–35. pmid:4750913
- View Article
- PubMed/NCBI
- Google Scholar
11. Verberckmoes SC, Persy V, Behets GJ, Neven E, Hufkens A, et al. (2007) Uremia-related vascular calcification: more than apatite deposition. Kidney Int 71: 298–303. pmid:17149373
- View Article
- PubMed/NCBI
- Google Scholar
12. Schlieper G, Aretz A, Verberckmoes SC, Kruger T, Behets GJ, et al. (2010) Ultrastructural analysis of vascular calcifications in uremia. J Am Soc Nephrol 21: 689–96. pmid:20203159
- View Article
- PubMed/NCBI
- Google Scholar
13. Fischer DC, Behets GJ, Hakenberg OW, Voigt M, Vervaet BA, al. (2012) Arterial microcalcification in atherosclerotic patients with and without chronic kidney disease: a comparative high-resolution scanning X-ray diffraction analysis. Calcif Tissue Int 90: 465–72. pmid:22476351
- View Article
- PubMed/NCBI
- Google Scholar
14. Montezano AC, Zimmerman D, Yusuf H, Burger D, Chignalia AZ, et al. (2010) Vascular smooth muscle cell differentiation to an osteogenic phenotype involves TRPM7 modulation by magnesium. Hypertension 56: 453–62. pmid:20696983
- View Article
- PubMed/NCBI
- Google Scholar
15. Salem S, Bruck H, Bahlmann FH, Peter M, Passlick-Deetjen J, et al. (2012) Relationship between magnesium and clinical biomarkers on inhibition of vascular calcification. Am J Nephrol 35: 31–9. pmid:22179063
- View Article
- PubMed/NCBI
- Google Scholar
16. Kircelli F, Peter ME, Sevinc OE, Celenk FG, Yilmaz M, et al. (2012) Magnesium reduces calcification in bovine vascular smooth muscle cells in a dose-dependent manner. Nephrol Dial Transplant 27: 514–21. pmid:21750166
- View Article
- PubMed/NCBI
- Google Scholar
17. Louvet L, Buchel J, Steppan S, Passlick-Deetjen J, Massy ZA (2013) Magnesium prevents phosphate-induced calcification in human aortic vascular smooth muscle cells. Nephrol Dial Transplant 28: 869–78. pmid:23229924
- View Article
- PubMed/NCBI
- Google Scholar
18. Montes de Oca A, Guerrero F, Martinez-Moreno JM, Madueño JA, Herencia C, et al. (2014) Magnesium inhibits Wnt/β-catenin activity and reverses the osteogenic transformation of vascular smooth muscle cells. PLoS One 9: e89525. pmid:24586847
- View Article
- PubMed/NCBI
- Google Scholar
19. Legeros RZ (2001) Formation and transformation of calcium phosphates: relevance to vascular calcification. Z Kardiol 90 Suppl 3: 116–24. pmid:11374023
- View Article
- PubMed/NCBI
- Google Scholar
20. Legeros RZ, Contiguglia SR, Alfrey AC (1973) Pathological calcifications associated with uremia: two types of calcium phosphate deposits. Calcif Tissue Res 13: 173–85. pmid:4792081
- View Article
- PubMed/NCBI
- Google Scholar
21. Bennett RM, Lehr JR, McCarty DJ F (1975) Actors affecting the solubility of calcium pyrophosphate dihydrate crystals. J Clin Invest 56: 1571–9. pmid:423
- View Article
- PubMed/NCBI
- Google Scholar
22. Boskey AL, Posner AS (1980) Effect of magnesium on lipid-induced calcification: an in vitro model for bone mineralization. Calcif Tissue Int 32: 139–43. pmid:6773631
- View Article
- PubMed/NCBI
- Google Scholar
23. Termine JD, Peckauskas RA, Posner AS (1970) Calcium phosphate formation in vitro. II. Effects of environment on amorphous-crystalline transformation. Arch Biochem Biophys 140: 318–25. pmid:4319593
- View Article
- PubMed/NCBI
- Google Scholar
24. Rey C, Combes C, Drouet C, Sfihi H, Barroug A (2007);Physico-chemical properties of nanocrystalline apatites: implications for biominerals and biomaterials. Materials Science and Engineering C 27: 198–205.
- View Article
- Google Scholar
25. Bonewald LF, Harris SE, Rosser J, Dallas MR, Dallas SL, et al. (2003) Von Kossa staining alone is not sufficient to confirm that mineralization in vitro represents bone formation. Calcif Tissue Int 72: 537–47. pmid:12724828
- View Article
- PubMed/NCBI
- Google Scholar
26. Sattlecker M, Baker R, Stone N, Bessant C (2011) Support vector machine ensembles for breast cancer type prediction from mid-FTIR micro-calcification spectra. Chemometrics Intell Lab Syst 107: 363.
- View Article
- Google Scholar
27. Bazin D, Daudon M, Combes C, Rey C (2012) Characterization and some physicochemical aspects of pathological microcalcifications. Chem Rev 112: 5092–120. pmid:22809072
- View Article
- PubMed/NCBI
- Google Scholar
28. Skalli O, Pelte MF, Peclet MC, Gabbiani G, Gugliotta P, et al. (1989) Alpha-smooth muscle actin, a differentiation marker of smooth muscle cells, is present in microfilamentous bundles of pericytes. J Histochem Cytochem 37: 315–21. pmid:2918221
- View Article
- PubMed/NCBI
- Google Scholar
29. Meade AD, Lyng FM, Knief P, Byrne HJ (2007) Growth substrate induced functional changes elucidated by FTIR and Raman spectroscopy in in-vitro cultured human keratinocytes. Anal Bioanal Chem 387: 1717–28. pmid:17102969
- View Article
- PubMed/NCBI
- Google Scholar
30. Gazi E, Dwyer J, Lockyer NP, Miyan J, Gardner P, et al. (2005) Fixation protocols for subcellular imaging by synchrotron-based Fourier transform infrared microspectroscopy. Biopolymers 77: 18–30. pmid:15558657
- View Article
- PubMed/NCBI
- Google Scholar
31. Shen M, Lajos PS, Farge D, Daudon M, Carpentier SM, et al. (1998) I.R. spectroscopy in the evaluation of the process of calcification of valvular bioprostheses. The Annals of Thoracic Surgery 66: S236.
- View Article
- Google Scholar
32. Estepa L, Daudon M (1997) Contribution of F.T.—I.R. spectroscopy to the identification of urinary stones and kidney crystal deposits. Biospectroscopy 3: 347.
- View Article
- Google Scholar
33. Filik J, Frogley MD, Pijanka JK, Wehbe K, Cinque G (2012) Electric field standing wave artefacts in FTIR micro-spectroscopy of biological materials. Analyst 137: 853–61. pmid:22231204
- View Article
- PubMed/NCBI
- Google Scholar
34. Bassan P, Lee J, Sachdeva A, Pissardini J, Dorling KM, et al. (2013) The inherent problem of transflection-mode infrared spectroscopic microscopy and the ramifications for biomedical single point and imaging applications. Analyst 138: 144–57. pmid:23099638
- View Article
- PubMed/NCBI
- Google Scholar
35. Wehbe K, Filik J, Frogley MD, Cinque G (2013) The effect of optical substrates on micro-FTIR analysis of single mammalian cells. Anal Bioanal Chem 405: 1311–24. pmid:23151654
- View Article
- PubMed/NCBI
- Google Scholar
36. Bazin D, Chappard C, Combes C, Carpentier X, Rouzière S, et al. (2009) Diffraction techniques and vibrational spectroscopy opportunities to characterise bones. Osteoporos Int 20: 1065. pmid:19340497
- View Article
- PubMed/NCBI
- Google Scholar
37. Shepherd JH, Shepherd DV, Best SM (2012) Substituted hydroxyapatites for bone repair. J Mater Sci: Mater Med 23: 2335.
- View Article
- Google Scholar
38. Ibrahim DM, Mostafa AA, Korowash SI (2011) Chemical characterization of some substituted HAP. Chemistry Central J 5: 74.
- View Article
- Google Scholar
39. Salimi MH, Heughebaert JC, Nancollas GH (1985) Crystal growth of Ca phosphates in the presence of Mg ions. Langmuir 1: 119.
- View Article
- Google Scholar
40. Wang L, Nancollas GH (2008) Ca orthophosphates: crystallization and dissolution. Chem. Rev 106: 4628.
- View Article
- Google Scholar
41. Lomashvili KA, Cobbs S, Hennigar RA, Hardcastle KI, O’Neill WC (2004) Phosphate-induced vascular calcification: role of pyrophosphate and osteopontin. J Am Soc Nephrol 15: 1392–401. pmid:15153550
- View Article
- PubMed/NCBI
- Google Scholar
42. Oh J, Wunsch R, Turzer M, Bahner M, Raggi P, et al. (2002) Advanced coronary and carotid arteriopathy in young adults with childhood-onset chronic renal failure. Circulation 106: 100–5. pmid:12093777
- View Article
- PubMed/NCBI
- Google Scholar
43. Eifinger F, Wahn F, Querfeld U, Pollok M, Gevargez A, et al. (2000) Coronary artery calcifications in children and young adults treated with renal replacement therapy. Nephrol Dial Transplant 15: 1892–4. pmid:11071992
- View Article
- PubMed/NCBI
- Google Scholar
44. Goodman WG, Goldin J, Kuizon BD, Yoon C, Gales B, et al. (2000) Coronary-artery calcification in young adults with end-stage renal disease who are undergoing dialysis. N Engl J Med 342: 1478–83. pmid:10816185
- View Article
- PubMed/NCBI
- Google Scholar
45. Becker A, Epple M, Müller KM, Schmitz I (2004) A comparative study of clinically4 well-characterized human atherosclerotic plaques with histological, chemical, and 5 ultrastructural methods. J Inorg Biochem 98: 2032–8. pmid:15541492
- View Article
- PubMed/NCBI
- Google Scholar
46. Hamad M, Heughebaeret JC (1986) The growth of whitlockite. J. Crystal Growth 79: 192–7.
- View Article
- Google Scholar
47. Montel G, Bonel G, Heughebaert JC, Trombe JC, Rey C (1981) New concepts in the composition, crystallization and growth of the mineral component of calcified tissues. J. Crystal Growth 53: 74–99.
- View Article
- Google Scholar
48. De Schutter TM, Behets GJ, Geryl H, Peter ME, Steppan S, et al. (2013) Effect of a magnesium-based phosphate binder on medial calcification in a rat model of uremia. Kidney Int 83:1109–17. pmid:23486515
- View Article
- PubMed/NCBI
- Google Scholar
49. Massy ZA, Ivanovski O, Nguyen-Khoa T, Angulo J, Szumilak D, et al. (2005) Uremia accelerates both atherosclerosis and arterial calcification in apolipoprotein E knockout mice. J Am Soc Nephrol 16: 109–16. pmid:15563564
- View Article
- PubMed/NCBI
- Google Scholar
50. Proudfoot D, Skepper JN, Hegyi L, Bennett MR, Shanahan CM, et al. (2000) Apoptosis regulates human vascular calcification in vitro: evidence for initiation of vascular calcification by apoptotic bodies. Circ Res 87: 1055–62. pmid:11090552
- View Article
- PubMed/NCBI
- Google Scholar
51. Massy ZA, Drüeke TB (2012) Magnesium and outcomes in patients with chronic kidney disease: focus on vascular calcification, atherosclerosis and survival. Clin Kidney J 5 Suppl 1: i52 i61.
- View Article
- Google Scholar

[ref1] 1. Takasu J, Budoff MJ, Katz R, Rivera JJ, O’Brien KD, et al. (2010) Relationship between common carotid intima-media thickness and thoracic aortic calcification: the Multi-Ethnic Study of Atherosclerosis. Atherosclerosis 209: 142–6. pmid:19782983
View Article
PubMed/NCBI
Google Scholar

[2] View Article

[3] PubMed/NCBI

[4] Google Scholar

[ref2] 2. Ishiyama M, Suzuki E, Katsuda J, Murase H, Tajima Y, et al. (2009) Associations of coronary artery calcification and carotid intima-media thickness with plasma concentrations of vascular calcification inhibitors in type 2 diabetic patients. Diabetes Res Clin Pract 85: 189–96. pmid:19497632
View Article
PubMed/NCBI
Google Scholar

[6] View Article

[7] PubMed/NCBI

[8] Google Scholar

[ref3] 3. Braun J, Oldendorf M, Moshage W, Heidler R, Zeitler E, et al. (1996) Electron beam computed tomography in the evaluation of cardiac calcification in chronic dialysis patients. Am J Kidney Dis Mar;27(3):394–401.
View Article
Google Scholar

[10] View Article

[11] Google Scholar

[ref4] 4. London GM, Guerin AP, Marchais SJ, Metivier F, Pannier B, et al. (2003) Arterial media calcification in end-stage renal disease: impact on all-cause and cardiovascular mortality. Nephrol Dial Transplant 18: 1731–40. pmid:12937218
View Article
PubMed/NCBI
Google Scholar

[13] View Article

[14] PubMed/NCBI

[15] Google Scholar

[ref5] 5. Noordzij M, Cranenburg EM, Engelsman LF, Hermans MM, Boeschoten EW, et al. (2011) Progression of aortic calcification is associated with disorders of mineral metabolism and mortality in chronic dialysis patients. Nephrol Dial Transplant 26: 1662–9. pmid:20880929
View Article
PubMed/NCBI
Google Scholar

[17] View Article

[18] PubMed/NCBI

[19] Google Scholar

[ref6] 6. Moe SM, Chen NX (2004) Pathophysiology of vascular calcification in chronic kidney disease. Circ Res 95: 560–7. pmid:15375022
View Article
PubMed/NCBI
Google Scholar

[21] View Article

[22] PubMed/NCBI

[23] Google Scholar

[ref7] 7. Villa-Bellosta R, Millan A, Sorribas V (2011) Role of calcium-phosphate deposition in vascular smooth muscle cell calcification. Am J Physiol Cell Physiol 300: C210 C220. pmid:20881235
View Article
PubMed/NCBI
Google Scholar

[25] View Article

[26] PubMed/NCBI

[27] Google Scholar

[ref8] 8. Sage AP, Lu J, Tintut Y, Demer LL (2011) Hyperphosphatemia-induced nanocrystals upregulate the expression of bone morphogenetic protein-2 and osteopontin genes in mouse smooth muscle cells in vitro. Kidney Int 79: 414–22. pmid:20944546
View Article
PubMed/NCBI
Google Scholar

[29] View Article

[30] PubMed/NCBI

[31] Google Scholar

[ref9] 9. Reynolds JL, Joannides AJ, Skepper JN, McNair R, Schurgers LJ, et al. (2004) Human vascular smooth muscle cells undergo vesicle-mediated calcification in response to changes in extracellular calcium and phosphate concentrations: a potential mechanism for accelerated vascular calcification in ESRD. J Am Soc Nephrol 15:2857–67. pmid:15504939
View Article
PubMed/NCBI
Google Scholar

[33] View Article

[34] PubMed/NCBI

[35] Google Scholar

[ref10] 10. Contiguglia SR, Alfrey AC, Miller NL, Runnells DE, Le Geros RZ (1973) Nature of soft tissue calcification in uremia. Kidney Int 4: 229–35. pmid:4750913
View Article
PubMed/NCBI
Google Scholar

[37] View Article

[38] PubMed/NCBI

[39] Google Scholar

[ref11] 11. Verberckmoes SC, Persy V, Behets GJ, Neven E, Hufkens A, et al. (2007) Uremia-related vascular calcification: more than apatite deposition. Kidney Int 71: 298–303. pmid:17149373
View Article
PubMed/NCBI
Google Scholar

[41] View Article

[42] PubMed/NCBI

[43] Google Scholar

[ref12] 12. Schlieper G, Aretz A, Verberckmoes SC, Kruger T, Behets GJ, et al. (2010) Ultrastructural analysis of vascular calcifications in uremia. J Am Soc Nephrol 21: 689–96. pmid:20203159
View Article
PubMed/NCBI
Google Scholar

[45] View Article

[46] PubMed/NCBI

[47] Google Scholar

[ref13] 13. Fischer DC, Behets GJ, Hakenberg OW, Voigt M, Vervaet BA, al. (2012) Arterial microcalcification in atherosclerotic patients with and without chronic kidney disease: a comparative high-resolution scanning X-ray diffraction analysis. Calcif Tissue Int 90: 465–72. pmid:22476351
View Article
PubMed/NCBI
Google Scholar

[49] View Article

[50] PubMed/NCBI

[51] Google Scholar

[ref14] 14. Montezano AC, Zimmerman D, Yusuf H, Burger D, Chignalia AZ, et al. (2010) Vascular smooth muscle cell differentiation to an osteogenic phenotype involves TRPM7 modulation by magnesium. Hypertension 56: 453–62. pmid:20696983
View Article
PubMed/NCBI
Google Scholar

[53] View Article

[54] PubMed/NCBI

[55] Google Scholar

[ref15] 15. Salem S, Bruck H, Bahlmann FH, Peter M, Passlick-Deetjen J, et al. (2012) Relationship between magnesium and clinical biomarkers on inhibition of vascular calcification. Am J Nephrol 35: 31–9. pmid:22179063
View Article
PubMed/NCBI
Google Scholar

[57] View Article

[58] PubMed/NCBI

[59] Google Scholar

[ref16] 16. Kircelli F, Peter ME, Sevinc OE, Celenk FG, Yilmaz M, et al. (2012) Magnesium reduces calcification in bovine vascular smooth muscle cells in a dose-dependent manner. Nephrol Dial Transplant 27: 514–21. pmid:21750166
View Article
PubMed/NCBI
Google Scholar

[61] View Article

[62] PubMed/NCBI

[63] Google Scholar

[ref17] 17. Louvet L, Buchel J, Steppan S, Passlick-Deetjen J, Massy ZA (2013) Magnesium prevents phosphate-induced calcification in human aortic vascular smooth muscle cells. Nephrol Dial Transplant 28: 869–78. pmid:23229924
View Article
PubMed/NCBI
Google Scholar

[65] View Article

[66] PubMed/NCBI

[67] Google Scholar

[ref18] 18. Montes de Oca A, Guerrero F, Martinez-Moreno JM, Madueño JA, Herencia C, et al. (2014) Magnesium inhibits Wnt/β-catenin activity and reverses the osteogenic transformation of vascular smooth muscle cells. PLoS One 9: e89525. pmid:24586847
View Article
PubMed/NCBI
Google Scholar

[69] View Article

[70] PubMed/NCBI

[71] Google Scholar

[ref19] 19. Legeros RZ (2001) Formation and transformation of calcium phosphates: relevance to vascular calcification. Z Kardiol 90 Suppl 3: 116–24. pmid:11374023
View Article
PubMed/NCBI
Google Scholar

[73] View Article

[74] PubMed/NCBI

[75] Google Scholar

[ref20] 20. Legeros RZ, Contiguglia SR, Alfrey AC (1973) Pathological calcifications associated with uremia: two types of calcium phosphate deposits. Calcif Tissue Res 13: 173–85. pmid:4792081
View Article
PubMed/NCBI
Google Scholar

[77] View Article

[78] PubMed/NCBI

[79] Google Scholar

[ref21] 21. Bennett RM, Lehr JR, McCarty DJ F (1975) Actors affecting the solubility of calcium pyrophosphate dihydrate crystals. J Clin Invest 56: 1571–9. pmid:423
View Article
PubMed/NCBI
Google Scholar

[81] View Article

[82] PubMed/NCBI

[83] Google Scholar

[ref22] 22. Boskey AL, Posner AS (1980) Effect of magnesium on lipid-induced calcification: an in vitro model for bone mineralization. Calcif Tissue Int 32: 139–43. pmid:6773631
View Article
PubMed/NCBI
Google Scholar

[85] View Article

[86] PubMed/NCBI

[87] Google Scholar

[ref23] 23. Termine JD, Peckauskas RA, Posner AS (1970) Calcium phosphate formation in vitro. II. Effects of environment on amorphous-crystalline transformation. Arch Biochem Biophys 140: 318–25. pmid:4319593
View Article
PubMed/NCBI
Google Scholar

[89] View Article

[90] PubMed/NCBI

[91] Google Scholar

[ref24] 24. Rey C, Combes C, Drouet C, Sfihi H, Barroug A (2007);Physico-chemical properties of nanocrystalline apatites: implications for biominerals and biomaterials. Materials Science and Engineering C 27: 198–205.
View Article
Google Scholar

[93] View Article

[94] Google Scholar

[ref25] 25. Bonewald LF, Harris SE, Rosser J, Dallas MR, Dallas SL, et al. (2003) Von Kossa staining alone is not sufficient to confirm that mineralization in vitro represents bone formation. Calcif Tissue Int 72: 537–47. pmid:12724828
View Article
PubMed/NCBI
Google Scholar

[96] View Article

[97] PubMed/NCBI

[98] Google Scholar

[ref26] 26. Sattlecker M, Baker R, Stone N, Bessant C (2011) Support vector machine ensembles for breast cancer type prediction from mid-FTIR micro-calcification spectra. Chemometrics Intell Lab Syst 107: 363.
View Article
Google Scholar

[100] View Article

[101] Google Scholar

[ref27] 27. Bazin D, Daudon M, Combes C, Rey C (2012) Characterization and some physicochemical aspects of pathological microcalcifications. Chem Rev 112: 5092–120. pmid:22809072
View Article
PubMed/NCBI
Google Scholar

[103] View Article

[104] PubMed/NCBI

[105] Google Scholar

[ref28] 28. Skalli O, Pelte MF, Peclet MC, Gabbiani G, Gugliotta P, et al. (1989) Alpha-smooth muscle actin, a differentiation marker of smooth muscle cells, is present in microfilamentous bundles of pericytes. J Histochem Cytochem 37: 315–21. pmid:2918221
View Article
PubMed/NCBI
Google Scholar

[107] View Article

[108] PubMed/NCBI

[109] Google Scholar

[ref29] 29. Meade AD, Lyng FM, Knief P, Byrne HJ (2007) Growth substrate induced functional changes elucidated by FTIR and Raman spectroscopy in in-vitro cultured human keratinocytes. Anal Bioanal Chem 387: 1717–28. pmid:17102969
View Article
PubMed/NCBI
Google Scholar

[111] View Article

[112] PubMed/NCBI

[113] Google Scholar

[ref30] 30. Gazi E, Dwyer J, Lockyer NP, Miyan J, Gardner P, et al. (2005) Fixation protocols for subcellular imaging by synchrotron-based Fourier transform infrared microspectroscopy. Biopolymers 77: 18–30. pmid:15558657
View Article
PubMed/NCBI
Google Scholar

[115] View Article

[116] PubMed/NCBI

[117] Google Scholar

[ref31] 31. Shen M, Lajos PS, Farge D, Daudon M, Carpentier SM, et al. (1998) I.R. spectroscopy in the evaluation of the process of calcification of valvular bioprostheses. The Annals of Thoracic Surgery 66: S236.
View Article
Google Scholar

[119] View Article

[120] Google Scholar

[ref32] 32. Estepa L, Daudon M (1997) Contribution of F.T.—I.R. spectroscopy to the identification of urinary stones and kidney crystal deposits. Biospectroscopy 3: 347.
View Article
Google Scholar

[122] View Article

[123] Google Scholar

[ref33] 33. Filik J, Frogley MD, Pijanka JK, Wehbe K, Cinque G (2012) Electric field standing wave artefacts in FTIR micro-spectroscopy of biological materials. Analyst 137: 853–61. pmid:22231204
View Article
PubMed/NCBI
Google Scholar

[125] View Article

[126] PubMed/NCBI

[127] Google Scholar

[ref34] 34. Bassan P, Lee J, Sachdeva A, Pissardini J, Dorling KM, et al. (2013) The inherent problem of transflection-mode infrared spectroscopic microscopy and the ramifications for biomedical single point and imaging applications. Analyst 138: 144–57. pmid:23099638
View Article
PubMed/NCBI
Google Scholar

[129] View Article

[130] PubMed/NCBI

[131] Google Scholar

[ref35] 35. Wehbe K, Filik J, Frogley MD, Cinque G (2013) The effect of optical substrates on micro-FTIR analysis of single mammalian cells. Anal Bioanal Chem 405: 1311–24. pmid:23151654
View Article
PubMed/NCBI
Google Scholar

[133] View Article

[134] PubMed/NCBI

[135] Google Scholar

[ref36] 36. Bazin D, Chappard C, Combes C, Carpentier X, Rouzière S, et al. (2009) Diffraction techniques and vibrational spectroscopy opportunities to characterise bones. Osteoporos Int 20: 1065. pmid:19340497
View Article
PubMed/NCBI
Google Scholar

[137] View Article

[138] PubMed/NCBI

[139] Google Scholar

[ref37] 37. Shepherd JH, Shepherd DV, Best SM (2012) Substituted hydroxyapatites for bone repair. J Mater Sci: Mater Med 23: 2335.
View Article
Google Scholar

[141] View Article

[142] Google Scholar

[ref38] 38. Ibrahim DM, Mostafa AA, Korowash SI (2011) Chemical characterization of some substituted HAP. Chemistry Central J 5: 74.
View Article
Google Scholar

[144] View Article

[145] Google Scholar

[ref39] 39. Salimi MH, Heughebaert JC, Nancollas GH (1985) Crystal growth of Ca phosphates in the presence of Mg ions. Langmuir 1: 119.
View Article
Google Scholar

[147] View Article

[148] Google Scholar

[ref40] 40. Wang L, Nancollas GH (2008) Ca orthophosphates: crystallization and dissolution. Chem. Rev 106: 4628.
View Article
Google Scholar

[150] View Article

[151] Google Scholar

[ref41] 41. Lomashvili KA, Cobbs S, Hennigar RA, Hardcastle KI, O’Neill WC (2004) Phosphate-induced vascular calcification: role of pyrophosphate and osteopontin. J Am Soc Nephrol 15: 1392–401. pmid:15153550
View Article
PubMed/NCBI
Google Scholar

[153] View Article

[154] PubMed/NCBI

[155] Google Scholar

[ref42] 42. Oh J, Wunsch R, Turzer M, Bahner M, Raggi P, et al. (2002) Advanced coronary and carotid arteriopathy in young adults with childhood-onset chronic renal failure. Circulation 106: 100–5. pmid:12093777
View Article
PubMed/NCBI
Google Scholar

[157] View Article

[158] PubMed/NCBI

[159] Google Scholar

[ref43] 43. Eifinger F, Wahn F, Querfeld U, Pollok M, Gevargez A, et al. (2000) Coronary artery calcifications in children and young adults treated with renal replacement therapy. Nephrol Dial Transplant 15: 1892–4. pmid:11071992
View Article
PubMed/NCBI
Google Scholar

[161] View Article

[162] PubMed/NCBI

[163] Google Scholar

[ref44] 44. Goodman WG, Goldin J, Kuizon BD, Yoon C, Gales B, et al. (2000) Coronary-artery calcification in young adults with end-stage renal disease who are undergoing dialysis. N Engl J Med 342: 1478–83. pmid:10816185
View Article
PubMed/NCBI
Google Scholar

[165] View Article

[166] PubMed/NCBI

[167] Google Scholar

[ref45] 45. Becker A, Epple M, Müller KM, Schmitz I (2004) A comparative study of clinically4 well-characterized human atherosclerotic plaques with histological, chemical, and 5 ultrastructural methods. J Inorg Biochem 98: 2032–8. pmid:15541492
View Article
PubMed/NCBI
Google Scholar

[169] View Article

[170] PubMed/NCBI

[171] Google Scholar

[ref46] 46. Hamad M, Heughebaeret JC (1986) The growth of whitlockite. J. Crystal Growth 79: 192–7.
View Article
Google Scholar

[173] View Article

[174] Google Scholar

[ref47] 47. Montel G, Bonel G, Heughebaert JC, Trombe JC, Rey C (1981) New concepts in the composition, crystallization and growth of the mineral component of calcified tissues. J. Crystal Growth 53: 74–99.
View Article
Google Scholar

[176] View Article

[177] Google Scholar

[ref48] 48. De Schutter TM, Behets GJ, Geryl H, Peter ME, Steppan S, et al. (2013) Effect of a magnesium-based phosphate binder on medial calcification in a rat model of uremia. Kidney Int 83:1109–17. pmid:23486515
View Article
PubMed/NCBI
Google Scholar

[179] View Article

[180] PubMed/NCBI

[181] Google Scholar

[ref49] 49. Massy ZA, Ivanovski O, Nguyen-Khoa T, Angulo J, Szumilak D, et al. (2005) Uremia accelerates both atherosclerosis and arterial calcification in apolipoprotein E knockout mice. J Am Soc Nephrol 16: 109–16. pmid:15563564
View Article
PubMed/NCBI
Google Scholar

[183] View Article

[184] PubMed/NCBI

[185] Google Scholar

[ref50] 50. Proudfoot D, Skepper JN, Hegyi L, Bennett MR, Shanahan CM, et al. (2000) Apoptosis regulates human vascular calcification in vitro: evidence for initiation of vascular calcification by apoptotic bodies. Circ Res 87: 1055–62. pmid:11090552
View Article
PubMed/NCBI
Google Scholar

[187] View Article

[188] PubMed/NCBI

[189] Google Scholar

[ref51] 51. Massy ZA, Drüeke TB (2012) Magnesium and outcomes in patients with chronic kidney disease: focus on vascular calcification, atherosclerosis and survival. Clin Kidney J 5 Suppl 1: i52 i61.
View Article
Google Scholar

[191] View Article

[192] Google Scholar

Figures

Abstract

Background

Methodology/Principal Findings

Conclusions/Significance

Introduction

Material and Methods

Cell culture of HAVSMC

Calcification assays and sample preparation on MirrIR slides

Specific controls

Field Effect Scanning Electron Microscope (FE—SEM)

Energy Dispersive X-ray spectrometry (EDX)

FTIR spectroscopy

Results

Preliminary results

Ca2+ and Pi induce the formation of hydroxyapatite crystals on HAVSMC cell layer

Mg2+ does not modify Ca / Pi crystal structure and composition

Location of calcium phosphate apatite on HAVSMC cell layer

Passive Ca / Pi deposition on MirrIR slides

Effect of Mg2+ on crystal formation

Discussion

Supporting Information

S2 Fig. µFTIR maps (scale from blue to red with increasing concentration) of crystals generated in Pi4 or PiCa calcifying condition with or without magnesium (Mg2 and Mg5) at day 18 of incubation.

Acknowledgments

Author Contributions

References

Ca²⁺ and Pi induce the formation of hydroxyapatite crystals on HAVSMC cell layer

Mg²⁺ does not modify Ca / Pi crystal structure and composition

Effect of Mg²⁺ on crystal formation